Brass Life Expectancy

[JTB]

pinetreebbs,
neck annealing is the cure for split necks. however, split necks are caused by overworking the brass. this is normal with standard reloading dies because the die makers have no clue what brass you're going to use, which could have a large variation in neck thickness, so they make sure their standard dies squeeze the neck down to a minimum size. then the expander ball will open it back up to a couple of thousands under bullet diameter. that works the brass a lot.

eventually a few die makers, and Redding comes to mind among others offer what is a bushing die where the brass body is sized down as normal, but for the neck you pick a bushing diameter that will just squeeze the neck down a minimum amount that will let you seat the bullet with enough neck tension. there is no expander ball. you have to figure out which bushing to get based upon your brass. so the folks that use these are typically using them for target shooting, working on getting a maximum amount of reloads out of the brass, and hence usually only buy/reload brass all from the same lot and mfgr to get as high a uniformity as possible. So for them it's easier to pick a neck sizing bushing that will just size their brass only enough to hold the bullet and no more. since all the brass is from the same mfgr and lot, and usually so top quality brass, like Lapua, Peterson, Nosler, etc. the neck thickness is pretty uniform in that lot.

if you scrounge brass from anywhere and everywhere, multiple manufacturers, multiple lots, multiple firings, etc. you may need to just stick with a standard full length sizing die and just neck anneal every 3rd or 4th firing. in mixed case groups of ammo one shouldn't expect as uniform internal case volume and neck tension as when all the brass in the reloads came from one lot of brass from one manufacturer. that variation in internal volume and neck tension usually translates into more dispersion and larger groups due to velocity variations. so it's up to you how you want to do your reloading process, but if you're getting neck splits, it's time to either chuck the brass into the recycle bin or learn how to neck anneal and get the tooling required for that if you want to prolong the reloading life of the rest of the cases that didn't neck split.
-tdbru

I have been researching annealing and I ordered 200 pieces of new brass. I am just going to throw out my first batch I’ve been messing around with because it is all mixed matched at this point. It’s all loaded at the moment so I’ll toss it after firing or just put it away for just in case. I didn’t know any better at the time. My new brass arrived today. Another question to add to the thread. How would you prep your new brass? I am going to run it all through my sizing die. But will I see decrease in accuracy until after the first firing? It’s like working everything back up for the first time right?