"Houston, we have a problem"

[rasp65]

Hoot you did not say what type of brass it was you were using. In my case I checked everything I could as you did. I think the brass I had was over annealed giving it too soft a shoulder because I did not have any problems like this in the previous 1K rounds I had loaded.