08-15-2013, 02:06 AM
Did you read the link I posted regarding the phosphorus in nickel alloy? The conclusions drawn indicate the lower the phosphorus content, the less cracking there is. Since the 9310 contains a MAX 0.025% (could be less) and the AISI is mandated to be 0.03%.....